The Modified Koppers Vacuum Viscometer measures the viscosity of highly viscous materials according to ASTM D2171. Minimum sample volume is 2 mL. Minimum bath depth is 178 mm (7 in). Viscometers are provided with a certificate of calibration and instruction sheet. Holders are sold separately.
改良考伯斯逆流真空粘度計根據(jù)ASTM d 2171測量高粘性材料的粘度。小進樣量為2ml。小沐浴深度為178毫米(7英寸)。粘度計具有校準證書和說明書。
美國凱能改良考伯斯逆流真空玻璃粘度計技術(shù)參數(shù)：
Modified Koppers Vacuum Viscometer (Reversed Flow)
Catalog Number | Size | Approximate Constant (poise/sec at 300 mm Hg) | Viscosity Range (poise) | |||
Bulb B | Bulb C | Bulb D | Low | High | ||
9724-W50 | 25 | 2.0 | 1.0 | 0.7 | 42 | 800 |
9724-W55 | 50 | 8.0 | 4.0 | 3.0 | 180 | 3200 |
9724-W60 | 100 | 32 | 16 | 10 | 600 | 12800 |
9724-W65 | 200 | 128 | 64 | 40 | 2400 | 52000 |
9724-W70 | 400 | 500 | 250 | 160 | 9600 | 200000 |
美國Cannon凱能改良考伯斯逆流真空粘度計方法介紹：
美國Cannon玻璃毛細粘度管測試方法：ASTM D445, ASTM D446, ASTM D2170方法，透明和不透明液體運動粘度測定法 (包括計算動力粘度)，玻璃毛細管運動粘度計的規(guī)格及使用說明，瀝青運動粘度的試驗方法
原理：本法用以測定透明與不透明產(chǎn)品的粘度，它是在已知的溫度下，利用液體本身的重力流動性(gravity-flow)來測定一定體積的液體通過經(jīng)校正后的毛細玻璃管粘度計所需的時間。根據(jù)所測出的動力粘度可計算出公制粘度或粘度(dynamic viscosity)。
方法概要：取一定體積的液體在嚴格的溫度與固定的液面高度的控制下，使其流經(jīng)毛細管粘度計而計算其流經(jīng)時間。根據(jù)流經(jīng)時間與粘度計的校正常數(shù)的乘積即可得動力粘度。
所需儀器：
1. 粘度計: 校正過后的玻璃毛細管，其所測得的粘度能符合于所要求的復(fù)驗準確度再試準確度。
2. 粘度計支架: 能將粘度計在恒溫槽中架持穩(wěn)固，且能使其垂直豎立。
3. 粘度計調(diào)溫槽: 內(nèi)盛裝透明液體，能使樣品于粘度計內(nèi)較液面低20mm以下，或高于槽底20mm以上，能保持槽內(nèi)溫度的變動于15至100℃間低于±0.02℃的變化，在此溫度范圍以外，亦不超過±0.05℃的溫度變化。
4. 測溫器: 檢驗動力粘度計的溫度計內(nèi)盛有適當(dāng)?shù)囊后w，使之能符合溫度范圍，溫度計使用前均需校正，校正后準確度在±0.02℃，若其它測溫器有上述的精確度時亦可采用。
5. 定時器: 秒表或彈簧裝置的定時器均可使用，但其刻度至少在0.1秒，其測定200秒至900秒的誤差在±0.07%以內(nèi)。